Glossary entry (derived from question below)
Russian term or phrase:
травимость
English translation:
etchability , picklability
Added to glossary by
Jack Doughty
May 20, 2004 19:33
20 yrs ago
Russian term
травимость
Russian to English
Tech/Engineering
Metallurgy / Casting
Поскольку процесс азотирования реализуется при температуре от 800-900 до 400-450°С, структура сформированной нитридной зоны включает расположенную за сплошной зоной светлой травимости сплошную зону тёмной травимости.
I presume this has something to do with травление, but I can't find the word anywhere.
I presume this has something to do with травление, but I can't find the word anywhere.
Proposed translations
(English)
5 | etchability (abd some other senses) | ttagir |
4 | etching | Andrey Belousov (X) |
4 | bright etching || dark etching | Vladimir Pochinov |
Proposed translations
14 mins
Russian term (edited):
���������
Selected
etchability (abd some other senses)
E.g.,
high tensile modulus, and good chemical etchability are critical to ... www.dupont.com/kapton/applications/fpc-tab.htm
www.vacutrontechnologies.com/images/ genvac-itothinfilms.pdf
www.gouldelectronics.com/papers/ JW_TCR_PaperExpo03Vf.pdf
etc.
As for "темная" и "светлая" траимость, you may use "black etching" and "bright/clear etching".
BR
T.
--------------------------------------------------
Note added at 18 mins (2004-05-20 19:51:22 GMT)
--------------------------------------------------
Sorry!
other rfr-s
www.driftwoodart.com/pages/etching.html
www.kd7lmo.net/tech_pcb2.html
www.ets.ru/livelang/e47week.htm - IT IS A DICTIONARY! (... черновое ~ black pickling. чистое ~ clear etching; fine etching; finishing etching. щелочное ~ alkali dip; caustic etch. ...)
\"травимость\" is the feature of a material to be etched by certain solutions.
Yours
T.
--------------------------------------------------
Note added at 21 mins (2004-05-20 19:54:38 GMT)
--------------------------------------------------
One other and also close term is picklability (pls see www.fudetec.com/resumes/cvingin.pdf
pub99.ezboard.com/ fzsbottletheforumfrm40.showPrevMessage?topicID=5.topic
www.laar.uns.edu.ar/indexes/artic_v3204/p_281.pdf - very informative: \"STUDY OF THE PICKLABILITY OF 1.8 mm HOT-ROLLED STEEL STRIP IN ...\"
T.
high tensile modulus, and good chemical etchability are critical to ... www.dupont.com/kapton/applications/fpc-tab.htm
www.vacutrontechnologies.com/images/ genvac-itothinfilms.pdf
www.gouldelectronics.com/papers/ JW_TCR_PaperExpo03Vf.pdf
etc.
As for "темная" и "светлая" траимость, you may use "black etching" and "bright/clear etching".
BR
T.
--------------------------------------------------
Note added at 18 mins (2004-05-20 19:51:22 GMT)
--------------------------------------------------
Sorry!
other rfr-s
www.driftwoodart.com/pages/etching.html
www.kd7lmo.net/tech_pcb2.html
www.ets.ru/livelang/e47week.htm - IT IS A DICTIONARY! (... черновое ~ black pickling. чистое ~ clear etching; fine etching; finishing etching. щелочное ~ alkali dip; caustic etch. ...)
\"травимость\" is the feature of a material to be etched by certain solutions.
Yours
T.
--------------------------------------------------
Note added at 21 mins (2004-05-20 19:54:38 GMT)
--------------------------------------------------
One other and also close term is picklability (pls see www.fudetec.com/resumes/cvingin.pdf
pub99.ezboard.com/ fzsbottletheforumfrm40.showPrevMessage?topicID=5.topic
www.laar.uns.edu.ar/indexes/artic_v3204/p_281.pdf - very informative: \"STUDY OF THE PICKLABILITY OF 1.8 mm HOT-ROLLED STEEL STRIP IN ...\"
T.
4 KudoZ points awarded for this answer.
Comment: "Thank you. I think etchability is the most likely, and pickability also possible. Both words offend my sensibilities as to what the English language ought to be, but there you are, they exist, and ничего не поделаешь. :-(
Thanks also to Vladimir for his input."
3 mins
Russian term (edited):
���������
etching
etching - травление
2 mins
Russian term (edited):
���������
bright etching || dark etching
I think it's just the wrong use of the word by the Russian author.
--------------------------------------------------
Note added at 3 mins (2004-05-20 19:36:07 GMT)
--------------------------------------------------
Dark etching tests showed that no visible dark etching developed within a few hours ...
www.aps.anl.gov/xfd/communicator/user2000/rosenbergr3.pdf
--------------------------------------------------
Note added at 5 mins (2004-05-20 19:38:23 GMT)
--------------------------------------------------
ETCHABILITY
A bias introduced by etching could cause problems if etchability was correlated with specific sources. Comparison ...
www.geology.yale.edu/~brandon/Eprints/Bernet_etal2004a.pdf
--------------------------------------------------
Note added at 3 mins (2004-05-20 19:36:07 GMT)
--------------------------------------------------
Dark etching tests showed that no visible dark etching developed within a few hours ...
www.aps.anl.gov/xfd/communicator/user2000/rosenbergr3.pdf
--------------------------------------------------
Note added at 5 mins (2004-05-20 19:38:23 GMT)
--------------------------------------------------
ETCHABILITY
A bias introduced by etching could cause problems if etchability was correlated with specific sources. Comparison ...
www.geology.yale.edu/~brandon/Eprints/Bernet_etal2004a.pdf
Discussion